N06601 High Grade Nickel Based Alloy Pipe

Model NO.: N06601 Standard: AISI Technique: Cold Drawn Surface Treatment: Polished Application: Industrial Custom Sample: 5-7 Days Shipping Port: Shanghai Trademark: Tisco/Baosteel Specification: Dia 16 25 30 40mm * 6000mm length HS Code: 7222300000 Type: Round Composition: / Shape: Round Special Use: High-strength Steel Plate Sample: N06601 High Grade Nickel Based Alloy Pipe Certificate: ISO MOQ: 500kg Transport Package: Good Quality & Fumigated Wooden Box Origin: China N06601 High Grade Nickel Based Alloy Pipe Chemical Composition N06601 High Grade Nickel Based Alloy Pipe is outlined in the following table.

Element	Content (%)
Nickel, Ni	58-63
Chromium, Cr	21-25
Aluminum, Al	1-1.7
Copper, Cu	1
Manganese, Mn	1
Silicon, Si	0.5
Carbon, C	0.1
Sulfur, S	0.015
Iron, Fe	Balance

Physical Properties The following table shows the physical properties of N06601 High Grade Nickel Based Alloy Pipe.

Properties	Metric	Imperial
Density	8.11 g/cm3	0.293 lb/in3
Melting point	1360-1411°C	2480-2572°F

Mechanical Properties The mechanical properties of N06601 High Grade Nickel Based Alloy Pipe are displayed in the following table.

Properties	Metric	Imperial
Tensile strength (Solution annealed)	760 MPa	110000 psi
Yield strength (Solution annealed)	450 MPa	65300 psi
Elongation at break (Solution annealed)	42%	42%

Thermal Properties The thermal properties of N06601 High Grade Nickel Based Alloy Pipe are given in the following table.

Properties	Metric	Imperial
Thermal expansion co-efficient (@20-100°C/68-212°F)	13.75 µm/m°C	7.639 µin/in°F
Thermal conductivity	11.2 W/mK	77.7 BTU.in/hrft².°F

Fabrication and Heat Treatment Machinability Conventional machining techniques that are used for machining iron-based alloys can be used. Forming N06601 High Grade Nickel Based Alloy Pipe has excellent ductility, and can be readily formed by all conventional techniques. Welding The alloy can be welded using commonly used welding techniques such as gas-tungsten arc welding, shielded metal-arc welding, gas metal-arc welding and submerged-arc welding. Forging The alloy can be forged in the temperature range of 1038 to 1232°C (1900 to 2250°F). Hot Working Hot working of nicrofer 6023 alloy can be performed in the temperature range of 871 to 1232°C (1600 to 2250°F). Cold working Cold working may be performed using standard tooling. Annealing The alloy can be annealed at 1149°C (2100°F) and then rapidly cooled to avoid thermal cracking. Other Designations Other designations that are equivalent to nicrofer 6023 alloy include the following: AMS 5715 AMS 5870 ASTM B166 ASTM B167 ASTM B168 DIN 2.4851 Applications The following are the list of applications of nicrofer 6023 alloy: Annealing tubes Muffles Flame shields Combustor components Process heaters Condenser tubes   Stock

Form	Specification	Supply Form	Others
Sheet	Thickness:0.40-4.75mm,General Width:1000,1219,1500mm	Whole Coil or piece of it	Cold Annealed,Surface 2B,2E
Plate	Thickness:4.76-60mm,Width:1500,2000,2500mm,Length:3000,6000,8000,8500mm(Under 10mm plate can be coiled)	Whole Coil or piece of it	Single hot rolling,Solid solution annealed state,Surface 1D
Belt	Thickness:0.10-3.0mm,Width:50-500mm	Whole Coil or Specified size	Cold Annealed,Surface 2B,2E
Bar & Rod	Rolled barΦ5-45mm,Length≤1500mm	Polished Bar(circle,Square)	Solution annealing,descaling
	Forged barΦ26-245mm,Length≤4000mm
Weld tube	Outer diameterΦ4.76-135mm,Wall Thickness0.25-4.00mm,Length:≤35000 mm	Base on your requirement	Use for PHE
Seamless Tube	Outer diameterΦ3-114mm,Wall Thickness0.2-4.5mm	Base on your requirement	Use for PHE
Wire	Outer diameterΦ0.1-13mm	Base on your requirement	Ni & Ni Alloy, Ti & Ti Alloy
Forged piece	roundness and square alloy	Base on your requirement	Steel, Alloy
Flangs	All kinds of Flangs	Base on your requirement	Steel, Alloy
Welding Material	Coil wire Φ0.90mm/1.2mm/1.6mm	Base on your requirement	Certificate of Origin:America, Sweden, Britain, Germany, Austria, Italy, France.
	Straight WireΦ1.2mm/1.6mm/2.4mm/3.2mm/4.0mm
	Welding rodΦ2.4mm/3.2mm/4.0mm
Tube	Elbow, three links, four links, different diameter size	Base on your requirement	Ni & Ni alloy, Ti & Ti alloy
Explosive bonded laminate	Raw Sheet Thickness≥2mm	Base on your requirement	Ni & Ni alloy, Ti & Ti alloy

4. Contact us Name: Denny Cheng Direct line: 021-67897611  

Contact us if you need more details on N06601 Alloy Pipe. We are ready to answer your questions on packaging, logistics, certification or any other aspects about Round Pipe Tube、Nickel Alloy Pipe. If these products fail to match your need, please contact us and we would like to provide relevant information.