Model NO.: DIN X20CrMo13 Standard: AISI, ASTM, GB, JIS, DIN, BS Technique: Hot Worked Alloy: Alloy Key Word: Heat Resistant Steel Certificate: ISO9001:2008 Payment Term: L/C, T/T Delivery Term: Fob, CIF, CFR, Ex-Work, etc. Shape: Square Bar Trademark: Dongbei Special Steel Specification: customized sizes Type: Stainless Steel
Steel Grade: Stainless Steel Surface Treatment: Black or Bright Special Use: Stainless Steel Product Name: Mat.No. 1.4120 DIN X20crmo13 Heat Resistant Steel MOQ: 1 Ton Shipping: by Sea, Air Grade: Mat.No. 1.4120 DIN X20crmo13 Delivery Condition: Ar, N, T, Q, Tmcp, Q+T, Ut, Hic, Z Test Transport Package: Standard Seaworthy Package or as The Customers′ Re Origin: China Production Description:
1. Steel Grade: Mat.No. 1.4120 DIN X20CrMo13
2. Product name: Mat.No. 1.4120 DIN X20CrMo13 Heat Resistant Steel Bar
3. Length: 3000-12000mm or as required
4. Diameter: 3-2000mm
Steel DIN X20CrMo13(Mat.No. 1.4120, DIN X20CrMo13)
Designation by Standards
|Brand Name ||Ravne No. ||Mat. No. ||DIN ||EN ||AISI |
|PK320 ||320 ||1.4120 ||X20CrMo13 ||- ||- |
Chemical Composition (in weight %)
|C ||Si ||Mn ||Cr ||Mo ||Ni ||V ||W ||Others |
|2.05 ||0.25 ||0.30 ||11.50 ||- ||- ||- ||- ||- |
DIN X20CrMo13is stainless, heat resistant steel up to temperature of 550oC. Steel is resistant to water with a low chlorine content in fine-machined or, better still, polished condition.
Owing to its greater high-temperature strength and corrosion resistance - resulting from the addition of molybdenum - DIN X20CrMo13is used for shafts and blades in water and steam turbine systems. One special field of application is for bedknives in the cellulose industry.
Physical properties (avarage values) at ambient temperature
Modulus of elasticity [103x N/mm2]: Approx. 210
Density [g/cm3]: 7.7
Thermal conductivity [W/m.K]: 25.0
Electric resistivity [Ohm mm2/m]: 0.60
Specific heat capacity[J/g.K]: 0.43
Coefficient of Linear Thermal Expansion 10-6 oC-1
|20-100oC ||20-200oC ||20-300oC ||20-400oC ||20-500oC ||20-600oC ||20-700oC |
|11.7 ||12.0 ||12.4 ||12.9 ||13.3 ||13.6 ||14.0 |
Heat to 750-850oC, cool slowly in furnace. Tensile strength is max. 770 N/mm2. Structure is ferrite with spherical carbides.
Harden from a temperature of 950-1000oC followed by oil quenching.
Tempering temperature: 650-750oC, them air cooling. Structure is transformation structure with ferrite.
Mechanical properties at at ambient temperature
Condition: Quenched, d