Model NO.: 1.4313 Standard: ASTM, AISI, GB, JIS, DIN, BS Surface Treatment: Coated Application: Ship Plate, Boiler Plate, Container Plate, Flange Plate Stock: Stock Product Name: 1.4313 DIN X4crni134 AISI Ca6-Nm S41500 Stainless MOQ: 1 Ton Shipping: by Sea, Air Delivery Condition: Ar, N, T, Q, Tmcp, Q+T, Ut, Hic, Z Test Shape: Plate Transport Package: Standard Seaworthy Package or as The Customers′ Re Origin: China Type: Steel Plate
Certification: ISO, SGS, BV, RoHS, IBR Technique: Hot Rolled Special Use: High-strength Steel Plate Key Word: Stainless Steel
Plate Certificate: ISO9001:2008 Payment Term: L/C, T/T Delivery Term: Fob, CIF, CFR, Ex-Work, etc. Grade: 1.4313 DIN X4crni134 AISI Ca6-Nm S41500 Trademark: Baosteel Specification: customized sizes Production Description:
1. Steel Grade: 1.4313 DIN X4CrNi134 AISI CA6-NM S41500
2. Product name: 1.4313 DIN X4CrNi134 AISI CA6-NM S41500 Stainless Steel Plate
4.Heat Treatment: as required
Steel 1.4313 (Mat.No. 1.4313, DIN X4CrNi134, AISI CA6-NM)
Designation by Standards
|Brand Name ||Ravne No. ||Mat. No. ||DIN ||EN ||AISI |
|1.4313 ||340 ||1.4313 ||X4CrNi134 ||X3CrNiMo13-4 ||CA6-NM |
Chemical Composition (in weight %)
|C ||Si ||Mn ||Cr ||Mo ||Ni ||V ||W ||Others |
|max. 0.05 ||max. 0.60 ||max. 1.00 ||13.25 ||0.55 ||4.00 ||- ||- ||- |
Steel 1.4313 has a good strength and toughness properties in combination with good corrosion resistance and realiable weldability.
Steel is used for parts subjected to high mechanical stress in fittings and pump construction, for compressors and turbine in hydroelectric power station,and in crude oil and refrigerating systems.
Physical properties (avarage values) at ambient temperature
Modulus of elasticity [103x N/mm2]: 200, 185 (200oC), 170 (400oC)
Density [g/cm3]: 7.7
Thermal conductivity [W/m.K]: 25.0
Electric resistivity [Ohm mm2/m]: 0.6
Specific heat capacity[J/g.K]: 0.43
Coefficient of Linear Thermal Expansion 10-6oC-1
|20-100oC ||20-200oC ||20-300oC |
|10.5 ||10.9 ||11.6 |
Heat to 600-650oC, cool slowly in furnace.
Harden from a temperature of 950-1050oC followed by oil or air quenching.
QT 650: 650-700oC + 600-620oC
QT 780: 550-600oC
QT 900: 520-580oC
Structure after tempering is martensit with small ferrite component.
Mechanical properties at at ambient temperature
Hardness: 320 HB
Tensile strength: max. 1100 N/mm2
For QT 650
0.2% Proof Stress: 520 N/mm2
Tensile strength: 650-820 N/mm2
Elongation (A5): 15% (Longit., d
Contact us if you need more details on 1.4313. We are ready to answer your questions on packaging, logistics, certification or any other aspects about DIN X4crni134、AISI Ca6-Nm. If these products fail to match your need, please contact us and we would like to provide relevant information.
Product Categories : Alloy And Carbon Steel > Steel Plate